UV8L0367 - BASECOAT UV VAC.MET HR

FIELD OF APPLICATION:

Glossy UV varnish, suitable for both high vacuum metallization (with aluminum) and Sputtering - PVD with deposition of aluminum or other metals. Not suitable for outdoor applications.

PREPARATION OF THE SUBSTRATE:

Plastic materials: Directly on ABS, SAN after degreasing and on PP after flaming and primer.

PREPARATION OF THE PRODUCT:

Comp. A : UV8L0367 100 parts by weight Product ready for use. If needed: Diluent : 641 or 10002AE 30 - 50 parts by weight

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Single-component.

APPEARANCE OF THE FILM

Glossy

COLORS

Clear

SPECIFIC WEIGHT

0,99 kg/lt (± 0,04)

SUPPLY VISCOSITY

20” (± 1) ASTM 4 at 20 °C

DRY RESIDUE (A)

57% (± 1)

DRYING

Before UV curing, make sure the solvent is completely evaporated (Flash-Off with IR lamps for 3-4' at 50 °C). Use an ultraviolet (UV) lamp system for industrial curing that generates radiation in the 200-400 nm range with a power of 120W/cm. Such radiation must be properly focused on the workpiece. The curing time of UV coatings may vary from plant to plant.

RECOMMENDED LAYERS

2 coats

RECOMMENDED THICKNESS

15 - 20 µm

RECOATING:

Not recommended

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

In unopened and sealed packages, not exposed to the sun and kept at a temperature of +5 to +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.