2205M00095 - GLASSPLUS 2K WB MATT PAINT

FIELD OF APPLICATION:

Glass protection and decoration paint, characterized by high opacity, adhesion, surface hardness and water resistance to perfume and cream. Also suitable for metal substrates.

PREPARATION OF THE SUBSTRATE:

The surface to be painted must be free of contaminants. Flaming or ionization for glass.

PREPARATION OF THE PRODUCT:

Comp. A : 2205M00095 100 parts by weight Comp. B : CZW250 (standard) 30 parts by weight CZW270 (G1 resistant) 30 parts by weight Mix well for few minutes until smooth, preferably with mechanical stirrer Diluent: Demineralized water 20 - 40 parts by weight For applications on glass, add 1-3% Z.287 adhesion promoter. Coloring: For matte colors, use our PW series water-based pastes (25% max.), to be mixed with 2205M00095 before catalysis. For clear colors, use our 50100M/ZW300/DY80xxx series concentrates (20% max.), to be added and mixed together with comp. B.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Glossy

COLORS

Clear

SPECIFIC WEIGHT

1,07 kg/lt (±0,02)

SUPPLY VISCOSITY

55” (±5) at 25 °C ASTM 4

DRY RESIDUE (A)

36% (±2)

DRYING

Drying - Print-free: 4-5 hours. 5-10’ at 20 °C   Forced Drying 30’ at 130-150 °C   30-20’ at 160-170 °C 15-10’ at 180-190 °C

POT- LIFE at 20 °C

2 hours. The pot-life decreases at higher temperature.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Always carefully close CZW250/CZW270 containers immediately after use. Once the package is opened, use within 5 days. It can react with atmospheric moisture. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.