K.719 - MULTIGRIP - ACRILICO SEMIOPACO

FIELD OF APPLICATION:

High-quality top coat, especially suitable for direct coating of plastic substrates (ABS, ABS+PC, PUR. PU, PF), and also metals such as steel, galvanized steel, brass, zamak. Also recommended for glass applications, especially for outdoor display. Given the variety of glass on the market, a preliminary test of adhesion is always recommended.

High-quality semi-matt acrylic top coat, especially suitable for direct coating of plastic substrates (ABS, ABS+PC, PUR. PU, PF), and also metals such as steel, galvanized steel, brass, zamak. Also recommended for glass applications, especially for outdoor display. Given the variety of glass on the market, a preliminary test of adhesion is always recommended.

PREPARATION OF THE SUBSTRATE:

Iron or steel sheet metal: SA2 sandblasting or sanding followed by degreasing with solvents. Aluminum and light alloys: Sanding followed by degreasing with solvents. Galvanized sheet: Scouring with Scotch-Brite followed by degreasing with solvents. ABS, ABS-PC, PUR and thermosetting resins: Degreasing with suitable solvents.

RECOMMENDED PRIMERS:

See preparation substrate

PREPARATION OF THE SUBSTRATE:

Iron or steel sheet metal: SA2 sandblasting or sanding followed by degreasing with solvents. Aluminum and light alloys: Sanding followed by degreasing with solvents. Galvanized sheet: Scouring with Scotch-Brite followed by degreasing with solvents. ABS, ABS-PC, PUR and thermosetting resins: Degreasing with suitable solvents.

PREPARATION OF THE PRODUCT:

Comp. A: K.719 + Coloring Pastes 100 parts by weight Comp. B: CZ.265 15 or 20 parts by weight Or: CZ.711 (1) 20 parts by weight (1) Catalysis at 20% by weight with CZ.265 or CZ.711 is recommended if the finish is used as single coat. Doing so results in increased hardness, chemical and/or solvent resistance, and finally even a slight increase in gloss (2-4 Gloss). After adding pastes and mixing perfectly, catalyze according to the recommended ratios, then mix thoroughly until uniform color and consistency. Dilute with our thinners D.737 - D.219 (approx. 20% by weight on Component A) to a viscosity of 18”-20" Ford 4 at 20 °C.

PRODUCT SPECIFICATIONS:

PREPARATION OF THE PRODUCT:

Comp. A: K.719 + Coloring Pastes 100 parts by weight Comp. B: CZ.265 15 or 20 parts by weight Or: CZ.711 (1) 20 parts by weight (1) Catalysis at 20% by weight with CZ.265 or CZ.711 is recommended if the finish is used as single coat. Doing so results in increased hardness, chemical and/or solvent resistance, and finally even a slight increase in gloss (2-4 Gloss). After adding pastes and mixing perfectly, catalyze according to the recommended ratios, then mix thoroughly until uniform color and consistency. Dilute with our thinners D.737 - D.219 (approx. 20% by weight on Component A) to a viscosity of 18”-22" Ford 4 at 20 °C.

TYPE OF PRODUCT

Two-component;

PRODUCT SPECIFICATIONS:

APPEARANCE OF THE FILM

Semi-matte

TYPE OF PRODUCT

2K Acrylic Finishes

COLORS

By choice

APPEARANCE OF THE FILM

Semi-matt

DENSITY Comp. (A)

1,41 kg/lt (± 0,05)

COLORS

By choice

SUPPLY VISCOSITY

10" (± 2") Ford 8 at 25 °C

DENSITY Comp. (A)

1,41 kg/lt (± 0,05)

SOLID CONTENT

66% (± 2%)

SUPPLY VISCOSITY

12" (± 2") Ford 8 at 25 °C SOLID % - VOLUME (A+B) 48% (± 2%) SOLID % - WEIGHT (A+B) 66% (± 2%)

DRYING

Dry dust-free - Print-free: 4-5 hours. 10’ - 15’ at 20 °C - Dry to touch - Print-free: 4-5 hours. 2.5 - 3 hours - Forced Drying - Print-free: 4-5 hours. 50’ - 60’ at 70 °C

DRYING AT 20°C

Dry dust-free - Print-free: 4-5 hours. 10’ - 15’ - Dry to touch - Print-free: 4-5 hours. 2.5 - 3 hours - Forced Drying - Print-free: 4-5 hours. 50’ - 60’ at 70 °C

RECOMMENDED LAYERS

A cross coat

1 (cross layer)

OPACITY

35 Gloss (± 2) when applied as single coat

35 Gloss (± 2) when applied as single coat

THEORETICAL YIELD (2)

9,2 m2/lt or 6,6 m2/kg at 50 µm dry

9,6 m2/lt or 6,9 m2/kg at 50 µm dry

RECOMMENDED THICKNESS

40 - 50 µm

RECOMMENDED - DFT

40 - 50 µm

POT-LIFE AT 20 °C

4 hours. The pot-life decreases at higher temperatures (2) in 80/20 ratio with P.900

4 hours. The pot-life decreases at higher temperatures (2) in 80/20 ratio with P.900

RECOATING:

Wet-on-wet within 1 hour or, after 8 hours minimum and not more than 36 hours. After complete curing of the film, it is necessary to sand lightly before painting.

APPLICATION INSTRUCTIONS:

View pictograms Page 1.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

RECOATING:

Wet-on-wet within 1 hour or, after 8 hours minimum and not more than 36 hours. After complete curing of the film, it is necessary to sand lightly before painting.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 09/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 09/24 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.