application datasheet

application datasheet

Download sheet in pdf

701.00020 - ULTRALACK 2K TRASPARENTE LUCIDO

View Product Shelf Life

PREPARATION OF THE SUBSTRATE:

Remove all traces of grease, moisture, waxes, polishing pastes by thorough degreasing of the surface to be painted.

PREPARATION OF THE PRODUCT:

Comp. A : 701.00020 100 parts by weight or volume Comp. B : CZ.265 33 parts by weight or volume Or : CZ.777 Mix until uniform consistency and color; dilute with our D.219 or D.727 thinner to viscosity of 16"-20" Ford 4 at 20 °C. For electrostatic applications, use the same thinners, up to a viscosity of 14-16" Ford 4 at 20 °C (corresponding to a dilution of about 40%), and if necessary, add electrostatic additive Z.050, to the extent of 0,5% to 2% on the paint. (1) For applications on manufactured goods intended for outdoor use, consult Vernici Caldart R&D Laboratory for guidance on the most appropriate cycle to be performed.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Glossy

COLORS

Colorless

SPECIFIC WEIGHT

0,96 Kg/l (± 0,05)

SUPPLY VISCOSITY

33" (± 5") ASTM 4 at 20 °C

DRY RESIDUE (comp.A)

41% (± 2%)

DRYING

Dry dust-free - Print-free: 4-5 hours. 15’ – 20’ at 20 °C   Print-free 3 – 4 hours at 20 °C   Forced Drying 30’-45’ at 80 – 120 °C (2)

RECOMMENDED LAYERS

On/Two cross coats.

RECOMMENDED THICKNESS

35 - 40 micron (3)

THEORETICAL YIELD

6 - 7 m2/Kg

POT- LIFE AT 20 °C

2-3 hours. The pot-life decreases at higher temperatures. (2) To achieve the best performance in substrate adhesion, hardness, chemical and mechanical strengths, carry out drying at 110 °C - 120 °C; (3) Thickness recommended for applications on metals that tend to oxidize quickly, such as brass, copper, zinc; Pencil Hardness: HB (standard ISO 15184) on 100 microns of catalyzed paint, applied on glass and cured 2 hours at 65 °C.

RECOATING:

Wet-on-wet or after 12 hours minimum. When the film has completely hardened, the surface to be painted must be lightly sanded. NOTES: any slightly cloudy appearance of the paint in bulk and/or after addition of the hardener does not constitute a defect or abnormality of the paint.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 05/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.

Other products in PRODOTTI PER LEGHE

 > 2K ACRYLIC CLEAR COATS

701.00080

ULTRALACK 2K TRASP. LUC. NO STAGNO

Vernici per Metalizzazione Sputtering PVD
Leghe Metallo Plastica Vetro

704.00020

ULTRALACK 2K MATT

Leghe Metallo Plastica Vetro
 > STOVING CLEAR COATS 140 °C

801.14061

STOVING CLEAR COATS 140° GLOSS

Leghe Metallo Vetro

803.14063

STOVING CLEAR COATS 140° SEMI-MATT

Leghe Metallo Vetro

804.14062

STOVING CLEAR COATS 140° MATT

Leghe Metallo Vetro
 > STOVING CLEAR COATS 160 °C

820006

MATT EPOXY CLEAR COAT

Leghe Metallo Vetro

820011

GLOSS EPOXY CLEAR COAT

Leghe Metallo Vetro
 > NITRO-ACRYLIC CLEAR COAT

511.00050

GLOSS NITRO-ACRYLIC CLEAR COAT

Metallo
 > 2K CLEAR COATS

901.00020

2K GLOSS ACID-HARDENER CLEAR COAT

Leghe Metallo Vetro

904.00030

2K MATT ACID-HARDENER CLEAR COAT

Leghe Metallo Vetro