20023 - PRIMER ACRILICO 2K

View Product Shelf Life

PREPARATION OF THE SUBSTRATE:

Plastic materials: Cleaning / Degreasing

PREPARATION OF THE PRODUCT:

Comp. A: 20023 100 parts by volume Comp. B: 20102 15 parts by weight or volume Alternatively (*): CZ.265 20 parts by weight or volume Diluent: 274 70 – 80 parts by weight or volume In special cases, to eliminate distension defects, peel or bubbles, 5-10% of 10304R retardant should be added. (*) CZ.265 is recommended for painting polycarbonate.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Glossy

COLORS

Clear

SPECIFIC WEIGHT

Component A: 0,98 Kg/l (± 0,02)

DRY RESIDUE (A+ B)

64% (±2)

DRYING

Dry dust-free - Print-free: 4-5 hours. 30 - 40' at 20 °C. Complete curing at 20 °C - Print-free: 4-5 hours. 26 - 36 hours.   Forced Drying 30’ - 60’ at 50 - 60 °C.

RECOMMENDED LAYERS

A cross coat.

POT- LIFE at 20 °C

4 hours. The pot-life decreases at higher temperature.

RECOATING:

After 15' at room temperature or 30' at 50-60 °C.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 03/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.

Other products in FONDI E PRIMERS ANTICORROSIVI

 > ANTI-CORROSION ZINC-RICH PAINTS

194.70330

EPOZINC GREY

Metallo
 > HIGH ADHESION PRIMERS

66099

T-MOPLEN UV PRIMER

Leghe Metallo Plastica Vetro

994.11014

TOPFLEX BEIGE - WASH PRIMER

Leghe Metallo Vetro

994.90100

MONOFLEX BLACK - HIGH ADHESION PRIMERS

Leghe Metallo Vetro

994.90900

MONOFLEX WHITE - HIGH ADHESION PRIMERS

Leghe Metallo Vetro
 > EPOXY PRIMERS

190.70121

EPOFLEX INDUSTRIAL DARK GREY

Leghe Metallo Vetro

190.90900

EPOFLEX INDUSTRIAL WHITE

Leghe Metallo Vetro

190.91100

EPOFLEX INDUSTRIAL BLACK

Leghe Metallo Vetro

190.A7035

EPOFLEX INDUSTRIAL HS GREY RAL 7035

Leghe Metallo Vetro

190.R7035

EPOFLEX INDUSTRIAL GREY RAL 7035

Leghe Metallo Vetro

193.90901

EPOFLEX ZINC WHITE

Leghe Metallo Vetro

193.HS990

EPOFLEX HS ZINC WHITE

Leghe Metallo Vetro

193.R7042

EPOFLEX ZINC

Leghe Metallo Vetro
 > CLEAR EPOXY COATING

101.00001

IMPREGNATING PRIMER CLEAR

Cemento Leghe Metallo Vetro
 > QUICK AIR DRY PRIMERS

490.R7001

SINTOFLEX INDUSTRIAL GREY RAL 7001

494.R7035

SINTOFLEX ZINC RAL7035 - QUICK AIR-DRY PRIMER

Metallo
 > WATER-BASED PRIMERS

193W70121

EPOFLEX WATER-BASED GREY

Leghe Metallo Vetro

494WR7035

SINTOFLEX WATER-BASED GREY RAL.7035

Metallo

793W90900

ACRYLIC PRIMER 2K WHITE WB

Leghe Metallo Plastica Vetro
 > NITRO-CELLULOSE PRIMERS

594.70055

NITROFLEX

 > INDUSTRIAL ACRYLIC PRIMERS

792.70701

ANCHOR GRIGIO - FONDO ACRILICO 2K

792.90900

ANCHOR WHITE - INDUSTRIAL ACRYLIC PRIMER

793.70701

IPERFILLER GREY

Leghe Metallo Vetro

794.90901

LANDER WHITE - INDUSTRIAL ACRYLIC PRIMER

Leghe Metallo Plastica Vetro