application datasheet

application datasheet

Download sheet in pdf

704.00020 - ULTRALACK 2K TRASPARENTE OPACO

View Product Shelf Life

PREPARATION OF THE SUBSTRATE:

Remove all traces of grease, moisture, waxes, polishing pastes by thorough degreasing of the surface to be painted.

PREPARATION OF THE PRODUCT:

Comp. A: 704.00020 100 parts by weight Comp. B: CZ.265 15 parts by weight Or: CZ.777 15 parts by weight Mix until uniform consistency and color; dilute with our acrylic thinner D.737 or D.727 to viscosity of 16"-18" Ford 4 at 20 °C. For electrostatic applications, use the same thinners, up to a viscosity of 14"-16" Ford 4 at 20° C, and if necessary, add electrostatic additive Z.050, to the extent of 0,5% - 1% on the paint.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Matte.

COLORS

Colorless

SPECIFIC WEIGHT

0,95 Kg/l (± 0,05)

SUPPLY VISCOSITY

45" (± 5") Ford 8 at 20 °C

DRY RESIDUE (comp.A)

28% (± 2%).

DRYING

Dry dust-free - Print-free: 4-5 hours. 10’ - 15’ at 20 °C   Print-free 3 - 4 hours at 20 °C   Forced Drying 30’ at 70 - 80 °C

RECOMMENDED LAYERS

Two coats (one cross coat)

RECOMMENDED THICKNESS

40 - 50 micron (2)

THEORETICAL YIELD

7.3 m2/Kg-Lt at 30 microns dry

OPACITY

9 (± 2) Gloss.

POT- LIFE AT 20 °C

2 - 3 hours. The pot-life decreases at higher temperatures (2) Thickness recommended for applications on metals that tend to oxidize quickly, such as brass, copper, zinc.

RECOATING:

Wet-on-wet or after 12 hours minimum. When the film has completely hardened, the surface to be painted must be lightly sanded.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 03/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.

Other products in PRODOTTI PER LEGHE

 > 2K ACRYLIC CLEAR COATS

701.00020

ULTRALACK 2K GLOSS

Vernici per Metalizzazione Sputtering PVD
Leghe Metallo Plastica Vetro

701.00080

ULTRALACK 2K TRASP. LUC. NO STAGNO

Vernici per Metalizzazione Sputtering PVD
Leghe Metallo Plastica Vetro
 > STOVING CLEAR COATS 140 °C

801.14061

STOVING CLEAR COATS 140° GLOSS

Leghe Metallo Vetro

803.14063

STOVING CLEAR COATS 140° SEMI-MATT

Leghe Metallo Vetro

804.14062

STOVING CLEAR COATS 140° MATT

Leghe Metallo Vetro
 > STOVING CLEAR COATS 160 °C

820006

MATT EPOXY CLEAR COAT

Leghe Metallo Vetro

820011

GLOSS EPOXY CLEAR COAT

Leghe Metallo Vetro
 > NITRO-ACRYLIC CLEAR COAT

511.00050

GLOSS NITRO-ACRYLIC CLEAR COAT

Metallo
 > 2K CLEAR COATS

901.00020

2K GLOSS ACID-HARDENER CLEAR COAT

Leghe Metallo Vetro

904.00030

2K MATT ACID-HARDENER CLEAR COAT

Leghe Metallo Vetro