Protective varnish for acetate and cellulose acetate-propionate substrates. Excellent adhesion even on NYLON, ABS, SAN, Urea, Optyl substrates; Good adhesion on glass. Characterized by high gloss, adhesion, elasticity and good resistance to light and artificial sweat. Paint 20044A also can be used as pre/post metalization paint.
Plastic materials: Cleaning or tumbling.
Comp. A : 20044A 100 parts by weight Comp. B : 10091P 50 parts by weight Diluent: 276 - 252 - D.219 80 - 100 parts by weight (*) (*) At this dilution, the application viscosity turns out to be about 14" - 15" (ideal for eyewear), while, for applications with viscosities of 18" - 20", dilute to 50 - 60% In special cases, to eliminate distension defects, peel or bubbles, 5-10% of 10304R retardant should be added. It is advisable to conduct preliminary tests to determine the right amount of retardant to use.
Two-component;
Glossy
Clear
0,95 kg/lt (± 0,02)
18” (±2) at 20 °C ASTM 4
33% (±2)
Drying - Print-free: 4-5 hours. 60’ at 20 °C Forced Drying 100’ at 20 °C 60’ at 45 - 55 °C
A cross coat
> 4 hours. The pot-life decreases at higher temperature Ultimate chemical resistances are reached after 5 days (at 20 °C) after leaving the baking oven.
Strictly follow the instructions on the labeling and in the safety data sheet.
The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Always carefully close containers of 10091P immediately after use, once opened use within 5 days. It can react with atmospheric moisture. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.