ACQ8370 - GLASSCOAT CONVERTER 1K WB

FIELD OF APPLICATION:

As colored primer/finish in the painting of metal substrates. Excellent adhesion, flexibility and chemical resistance. The varnish also offers excellent adhesion on glass after the addition of a suitable adhesion promoter. For coloring, use: · Concentrates 50100M / ZW300 / DY80xxx series (recommended max. ratio 100:25) · PW series pastes (recommended max. ratio 70:30) To be mixed before dilution with water

PREPARATION OF THE SUBSTRATE:

The substrate should be free of any kind of surface contaminants, (lubricant, traces of oxidation, residues of waxes or polishing pastes, residues of substances from galvanic baths, etc.) so it should be treated with appropriate cleaning methods.

PREPARATION OF THE PRODUCT:

Comp. A : ACQ8370 + Coloring Pastes or Concentrates 100 parts by weight Comp. B : Z.287 (adhesion promoter) 1 - 3 parts by weight Diluent: Demineralized water 50 - 70 parts by weight

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Single-component.

APPEARANCE OF THE FILM

Glossy

COLORS

Clear

SPECIFIC WEIGHT

1,04 kg/lt (±0,02)

DRY RESIDUE (A)

43% (±2)

DRYING

Drying - Print-free: 4-5 hours. 10-15’ at 20 °C   Forced Drying 30’ at 130-150 °C

RECOMMENDED LAYERS

A cross coat

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Always carefully close containers immediately after use. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.