Industrial acrylic primer with remarkable fast drying, no sagging and no absorption of overcoated enamel. Characterized by excellent general adhesion on plastics of various kinds, including: ABS, ABS – PC, PMMA, filled Nylon (1) (PA6 – GF > 30%), PUR and rigid PVC. (1) Due to the wide variety of PA6-GF blends on the market, it is always recommended to conduct preliminary tests before proceeding with production.
ABS/PC, ABS, PUR, PVC, PA6-GF, PMMA: Degreasing with suitable solvents or detergents. PP: Flaming
Thoroughly mix component A until the color and consistency are uniform. Then mix with component B in the ratio indicated below. Comp. A: 792.90900 100 by weight Comp. B: HD431003 10 by weight CZ.711 10 by weight Or (2) 20102 10 by weight Diluent D.737 40 - 50 by weight (2) Recommended for painting PA6-GF For PP Substrates: Thoroughly mix components A and B until the color and consistency are uniform. Then add PP activator in the ratio given below. Comp. A: 792.90900 100 by weight Comp. B: CZ.711 10 by weight Activator PP603 50 by weight Diluent D.737 0 - 10 by weight
Two-component;
Matte.
White
1,75 Kg/l (± 0,05)
23” (± 3) DIN 8 at 25 °C
72% (± 2)
Dry dust-free - Print-free: 4-5 hours. 10’ at 20– 25 °C Forced Drying 30’ – 40’ at 60 °C
Two coats.
30 - 50 µm (3)
11,1 m2/Lt or 6,8 m2/Kg at 40 µm dry
2 hours. The pot-life decreases at higher temperatures. (3) Calculated in non-absorbent flat surface. Yield on mineral substrates is highly variable and depends on substrate absorption.
After a minimum of 30' at 60 °C or after 4 hours at room temperature (25 °C) with Base Coat our 374 series, or our 773 series, or our pastels 211 – 711 – 7H1 series.
Strictly follow the instructions on the labeling and in the safety data sheet.
The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 03/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.
792.70701
ANCHOR GRIGIO - FONDO ACRILICO 2K
VERNICI CALDART SRL © 2022 | P.IVA IT00759630965 | Privacy Policy | Cookies Policy | Ethical Code | Whistleblowing | Financing | SOFTWEB