Applicable directly to: Iron, Aluminum, Galvanized Iron and Light Alloys, Fiberglass.
Epoxy - Polyurethane and Acrylic finishes.
Iron surfaces: SA2 sandblasting, or thorough mechanical cleaning followed by degreasing with solvents. Hot-dip Galvanized Steel: Light sandblasting or alternatively sanding or buffing followed by degreasing with solvent. Aluminum: Mechanical cleaning by sandblasting (where possible), sanding or buffing followed by degreasing with solvents. Copper and brass: Remove any traces of oxidation by sanding or buffing followed by degreasing with solvents.
Comp. A: 193.HS990 100 parts by weight 3 parts by Volume Comp. B: CZ.105 or CZ.110 20 parts by weight 1 part by Volume Alternatively (*): CZ.155 20 parts by weight 1 part by Volume Diluent D.150 Standard 5 - 20 parts by weight D.160 Fast 5 - 20 parts by weight For large areas and/or cabin temperature > 30 °C, we recommend D.130 Slow thinner, which ensures excellent spreading and reabsorption Over spray. (*) Not recommended for zinc plated products. Mix to uniform consistency and color; dilute with our D.150 epoxy thinners to optimum viscosity depending on the application system and/or thickness to be achieved. Applicable with conventional spray, Airmix and Airless systems.
2K Epoxy Primer
Matte
White
1,74 Kg/Lt (± 0,05)
5000 ±750 mPas. 25 °C
56% (± 2)
73% (± 2)
Dry dust-free Print-free: 4-5 hours. 15’ - 20’ Print-free 5 hours In depth 24 - 36 hours at 20 °C Forced Drying 45’ at 60 - 80 °C
1 /2
70 - 100 µm
7 m2/Lt or 4,7 m2/Kg at 80 µm dry
6 hours.
See pictograms Page 1
With CZ.105: minimum 6 hours maximum 36 hours. With CZ.110: minimum 3 hours maximum 24 hours. After 48 hours, light sanding of the film is recommended to ensure good adhesion of the top coat.
Strictly follow the instructions on the labeling and in the safety data sheet.
The storage room must be dry and with a temperature between + 10 °C and +35 °C. Rev.: 03/24 The data and information contained in this sheet are the result of our experience and accurate laboratory test. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.