Anticorrosive primer of universal type, applicable on: iron, copper, aluminum, galvanized iron, fiberglass and light alloys.
Epoxy – Polyurethane and Acrylic finishes
Iron surfaces: SA2 sandblasting, or thorough mechanical cleaning followed by degreasing with solvents. Hot-dip Galvanized Steel: Light sandblasting or alternatively sanding or buffing followed by degreasing with solvent Aluminum: Mechanical cleaning by sandblasting (where possible) sanding or buffing followed by degreasing with solvents. Copper and brass: Remove any traces of oxidation by sanding or buffing followed by degreasing with solvents.
Comp. A: 193.90901 100 parts by weight 3 parts by Volume Comp. B: CZ.105 / CZ.110 / CZ.155 20 parts by weight 1 part by Volume Thinner D.150 Standard 5 - 20 parts by weight Thinner D.160 Fast For large surfaces and/or cabin temperature > 30 °C, we recommend D.130 Slow thinner, which ensures excellent spreading and reabsorption Over spray. Mix to uniform consistency and color; dilute with our D.150 epoxy thinners to optimum viscosity, depending on the application system and or thickness to be achieved. Applicable with conventional spray, Airmix and Airless systems.
Epoxy Primer 2K
Matt
White
1,65 Kg/Lt (± 0,05)
20” ±4 DIN 8 at 25 °C SOLID % - VOLUME (A+B) 55% (± 2) SOLID % - WEIGHT (A+B) 72% (± 2)
Dry dust-free Print-free: 4-5 hours. 15’ – 20’ Drying 24 – 36 hours Forced Drying 30’ - 40’ at 60 - 80 °C
1 (cross layers)
70 - 100 µm
6,9 m2/Lt-4,7 m2/Kg at 80 µm dry
8 hours.
View pictograms Page 1.
With CZ.105: minimum 4-6 hours maximum 36 hours. With CZ.110: minimum 3-4 hours maximum 24 hours. Data referred to standard application (70 µm) at 25 °C and 50% RH. After 48 hours, light sanding of the film is recommended to ensure good adhesion of the top coat.
Strictly follow the instructions on the labeling and in the safety data sheet.
The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev 01/24 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.
792.70701
ANCHOR GRIGIO - FONDO ACRILICO 2K
VERNICI CALDART SRL © 2022 | P.IVA IT00759630965 | Privacy Policy | Cookies Policy | Ethical Code | Whistleblowing | Financing | SOFTWEB