Anticorrosive primer with cathodic protection effect for steel.
Wide compatibility with epoxy primers and intermediates.
Iron surfaces: SA2.5 sandblasting.
Comp. A: 194.70330 100 parts by weight Comp. B: CZ.105 or CZ.110 10 parts by weight Mix until uniform consistency and color; dilute with our D.150 epoxy thinner to a viscosity of 20-22 Ford 4 at 20 °C.
Spray: Use nozzles of 1.4-1.8 mm and pressure of 4-5 atm. Brush/Roll: Dilute with D.150 until well distended.
Epoxy zinc primer 2K
Matt
Gray
2,90 Kg/L(± 0,05)
Thixotropic SOLID % - VOLUME (A+B) 54% (± 2) SOLID % - WEIGHT (A+B) 82% (± 2)
Dry dust-free - Print-free: 4-5 hours. 15’ – 20’ Drying 24 – 36 hours Forced Drying 30’ - 40’ at 60 - 80 °C
1 (cross layers)
60 - 80 µm
3,9 m2/Kg – 9,1 m2/Lt at 60 µm dry
6 hours.
View pictograms Page 1.
With hardener CZ.105: minimum 4 hours maximum 36 hours. With hardener CZ.110: minimum 2 hours maximum 24 hours.
Strictly follow the instructions on the labeling and in the safety data sheet.
The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 01/24 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.
792.70701
ANCHOR GRIGIO - FONDO ACRILICO 2K
VERNICI CALDART SRL © 2022 | P.IVA IT00759630965 | Privacy Policy | Cookies Policy | Ethical Code | Whistleblowing | Financing | SOFTWEB