Industrial acrylic primer, extremely versatile, with remarkable fast drying, no sagging and absorption of overcoated enamel. It can be used directly on the substrate, as it has excellent general adhesion on both metal and plastic substrates of various kinds, including: ABS, Thermosets (PF - MF - UF), filled Nylon (PA6 - GF > 30%), PUR and rigid PVC, fiberglass.
Iron surfaces: SA2 sandblasting, or thorough mechanical cleaning followed by degreasing with solvents. Galvanized iron: Light silica sandblasting or thorough buffing with red Scotch Brite followed by solvent cleaning. Aluminum: Light sandblasting, alternatively sanding or Thorough scouring with Scotch Brite followed by degreasing with solvents. Thermosetting resins, ABS, PUR, PVC: Degreasing with suitable solvents. Filled Nylon (PA6 – GF > 30%) flaming
Thoroughly mix component A until the color and consistency are uniform. Then mix with component B in the ratio indicated below. By weight volume Comp. A: 793.70701 100 parts 100 parts Comp. B: CZ.265 20 parts 33 parts Dilute the perfectly blended mixture to the desired viscosity with our polyacrylic or polyurethane thinners such as D.219 or D.737.
Two-component;
Matte.
Gray
1,60 Kg/l (± 0,05)
24” (± 3”) DIN 8 25 °C
77% (± 2%)
Dry dust-free - Print-free: 4-5 hours. 10’ at 20 °C - 25 °C - Forced Drying 30’ - 40’ at 60 °C - 70 °C
Two coats
40-80 µm (1)
3h. The pot-life decreases at higher temperatures
8,7 m2/Lt or 6 m2/Kg at 60 µm dry (1) depending on the nature of the substrate and the specific needs of the case.
After 30 minutes at 60 °C (2) or after 4 hours and within 12 hours at room temperature. When completely cured, light sanding is recommended. Wet-on-wet cycle also possible after minimum 30 minutes drying at 25 °C with acrylics series 712 ,713 and 719 and at least 1 hour with gloss enamels series 200 or series 700. (2) Data referred to an application of µm dry.
Strictly follow the instructions on the labeling and in the safety data sheet.
The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 03/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.
792.70701
ANCHOR GRIGIO - FONDO ACRILICO 2K