2205L00781 - GLASSPLUS 2K WB SHINING PAINT

View Product Shelf Life

FIELD OF APPLICATION:

Glass protection and decoration paint, characterized by high gloss, adhesion, surface hardness and water resistance to perfume and cream. Also suitable for metal substrates.

FIELD OF APPLICATION:

Glass protection and decoration paint, characterized by high gloss, adhesion, surface hardness and water resistance to perfume and cream. Also suitable for metal substrates.

PREPARATION OF THE SUBSTRATE:

The surface to be painted must be free of contaminants. Flaming or ionization for glass.

PREPARATION OF THE SUBSTRATE:

The surface to be painted must be free of contaminants. Flaming or ionization for glass.

PREPARATION OF THE PRODUCT:

Comp. A : 2205L00781 100 parts by weight Comp. B : CZW250 (standard) 30 parts by weight CZW270 (G1 resistant) 30 parts by weight Mix well for few minutes until smooth, preferably with mechanical stirrer Diluent: Demineralized water 20 - 40 parts by weight For applications on glass, add 1-3% Z.287 adhesion promoter. Coloring: For matte colors, use our PW series water-based pastes (25% max.), to be mixed with 2205L00781 before catalysis. For clear colors, use our 50100M/ZW300/DY80xxx series concentrates (20% max.), to be added and mixed together with comp. B.

PREPARATION OF THE PRODUCT:

Comp. A : 2205L00781 100 parts by weight Comp. B : CZW250 (standard) 30 parts by weight CZW270 (G1 resistant) 30 parts by weight Mix well for few minutes until smooth, preferably with mechanical stirrer Diluent: Demineralized water 20 - 40 parts by weight For applications on glass, add 1-3% Z.287 adhesion promoter. Coloring: For matte colors, use our PW series water-based pastes (25% max.), to be mixed with 2205L00781 before catalysis. For clear colors, use our 50100M/ZW300/DY80xxx series concentrates (20% max.), to be added and mixed together with comp. B.

PRODUCT SPECIFICATIONS:

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Glossy

APPEARANCE OF THE FILM

Glossy

COLORS

Clear

COLORS

Clear

SPECIFIC WEIGHT

1,04 kg/lt (±0,02)

SPECIFIC WEIGHT

1,04 kg/lt (±0,02)

SUPPLY VISCOSITY

100” (±10) at 25 °C ASTM 4

SUPPLY VISCOSITY

100” (±10) at 25 °C ASTM 4

DRY RESIDUE (A)

35.5% (±2)

DRY RESIDUE (A)

35.5% (±2)

DRYING

Drying - Print-free: 4-5 hours. 5-10’ at 20 °C   Forced Drying 30’ at 130-150 °C   30-20’ at 160-170 °C 15-10’ at 180-190 °C

DRYING

Drying - Print-free: 4-5 hours. 5-10’ at 20 °C   Forced Drying 30’ at 130-150 °C   30-20’ at 160-170 °C 15-10’ at 180-190 °C

POT- LIFE at 20 °C

2 hours. The pot-life decreases at higher temperature.

POT- LIFE at 20 °C

2 hours. The pot-life decreases at higher temperature.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.