ACQ880 - POLYTERM IDROTOP WB 130?C

FIELD OF APPLICATION:

Suitable for application to metal (iron, aluminum, brass, alloys in general). Also excellent as a protective and decorative paint for glass.

PREPARATION OF THE SUBSTRATE:

The surface to be painted must be free of contaminants. For glass applications, flaming where needed.

PREPARATION OF THE PRODUCT:

Comp. A : ACQ880 100 parts Comp. B : Z.287 Adhesion promoter 2,5 parts (in the case of applications on glass) Stir well Diluent: Demineralized water 60 – 80 parts The solution additivated with Z.287 is stable for 4 hours after preparation. NOTE: If necessary, the paint can be colored with our 50100M / ZW300 / DY80xxx series concentrate in the rate of 20% max. referring to 100 parts of undiluted paint, or with PW series pigmented pastes (20% max.) to be added and mixed with paint before dilution with water. Larger additions are also possible, however, we recommend preliminary testing of the suitability of the complete cycle before moving to industrial-scale production.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Single-component.

APPEARANCE OF THE FILM

Glossy

COLOUR

Clear

DRYING

Drying : 5 - 15’ - 25 °C Curing : 30’ at 130 °C – 140 °C

RECOMMENDED LAYERS

2 coats.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +25 °C. Always carefully close containers immediately after use. Protect from frost. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.