OPM001 - PRIMER PER METALLO 150?C

FIELD OF APPLICATION:

Paint for the protection and decoration of metal eyeglass frames. Suitable as a protective agent for objects, brass products, and general galvanic substrates (handles, fashion accessories, etc.) and titanium. After baking, it can be repainted with baked clearcoats type 820011-22L00501.

PREPARATION OF THE SUBSTRATE:

The substrate should be free of any kind of surface contaminants, (lubricant, traces of oxidation, residues of waxes or polishing pastes, residues of substances from galvanic baths, etc.) so it should be treated with appropriate cleaning methods.

PREPARATION OF THE PRODUCT:

Component A : OPM001 100 parts by weight Diluent : 00680 80 – 90 parts by weight The primer can be colored with concentrated solutions of 50100M series dyes (5-10% by weight) or P.EP series pigmented pastes (5-10% by weight). Suitable for electrostatic application.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Single-component.

APPEARANCE OF THE FILM

N.D.

COLORS

Clear.

SPECIFIC WEIGHT

0,99 Kg/l (± 0,02)

SUPPLY VISCOSITY

90” (±2) at 20 °C ASTM 4

DRY RESIDUE

28% (± 2)

DRYING

Dry dust-free - Print-free: 4-5 hours. 15 at 20 °C;   Forced drying 15-30’ at 150-160 °C.

RECOMMENDED LAYERS

A cross coat. NOTE: OPM001 always requires overcoating.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

In unopened and sealed packages, not exposed to the sun and kept at a temperature of +5 to +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.