20095A - VERNICE BRILLANTE MEDIO SOLIDO

FIELD OF APPLICATION:

Protective varnish for Grilamid, cellulose acetopropionate, ABS and Polycarbonate substrates. Characterized by high gloss, high filling, adhesion, elasticity and good resistance to light and artificial sweat. High tensile strength.

PREPARATION OF THE SUBSTRATE:

Plastic materials: Tumbling.

PREPARATION OF THE PRODUCT:

Comp. A : 20095A 100 parts by weight Comp. B : 20025A 50 parts by weight Diluent : 276 – 252 80 - 100 parts by weight In special cases, to eliminate distension defects, peel or bubbles, 5-10% of 10304R retardant should be added. It is advisable to conduct preliminary tests to determine the right amount of retardant to use.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Glossy

COLORS

Clear

SPECIFIC WEIGHT

0,98 kg/lt (± 0,05)

SUPPLY VISCOSITY

50” (±2) at 20 °C ASTM 4

DRY RESIDUE (A)

53% (±2)

DRYING

Drying - Print-free: 4-5 hours. 15’ at 20 °C   Forced Drying 120’ at 45 - 55 °C

RECOMMENDED LAYERS

A cross coat

POT- LIFE at 20 °C

90’ The pot-life decreases at higher temperature The final chemical resistances, are reached after 5 days (at 20 °C) after leaving the baking oven.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.