889008 - SMALTO EPOSSIDICO NERO OPACO

FIELD OF APPLICATION:

Paint for the protection and decoration of metal eyeglass frames. Also suitable for direct applications on metal substrates in general, where special performance is required in terms of adhesion and surface hardness.

PREPARATION OF THE SUBSTRATE:

The substrate should be free of any kind of surface contaminants, (lubricant, traces of oxidation, residues of waxes or polishing pastes, residues of substances from galvanic baths, etc.) so it should be treated with appropriate cleaning methods.

PREPARATION OF THE PRODUCT:

Comp. A : 889008 100 parts by weight Diluent : D.921 50 – 60 parts by weight In special cases where it is necessary to eliminate distension defects, peel, bubble formation, it is recommended to replace part of the thinner (5% to 10%) with retardant 10304R.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Single-component.

APPEARANCE OF THE FILM

Matte.

COLORS

Black

SPECIFIC WEIGHT

1,46 kg/lt (± 0,02)

SUPPLY VISCOSITY

6” (±2) ford 8 at 25 °C

DRY RESIDUE

50% (±2)

DRYING

Dry dust-free - Print-free: 4-5 hours. 15 at 20 °C;   Forced drying 45 at 180 °C;

RECOMMENDED LAYERS

Two– three coats

RECOMMENDED THICKNESS

8– 12 micron (dry film)

OPACITY

11 (±2) Gloss NOTE: OPM001 always requires overcoating.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

In unopened and sealed packages, not exposed to the sun and kept at a temperature of +5 to +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.