22M05836 - MATT ACRYLIC 1K METAL TOPCOAT LTHC

FIELD OF APPLICATION:

Paint for the protection and decoration of metal eyeglass frames. Suitable as protective agent for brass products and general galvanic substrates (handles, fashion accessories, etc.). Direct adhesion on metal, non-yellowing, high resistance characteristics to CASS test and ISO 12870 artificial sweat.

PREPARATION OF THE SUBSTRATE:

The substrate should be free of any kind of surface contaminants, (lubricant, traces of oxidation, residues of waxes or polishing pastes, residues of substances from galvanic baths, etc.) so it should be treated with appropriate cleaning methods.

PREPARATION OF THE PRODUCT:

Comp. A : 22M05836 100 parts by weight Diluent : TH05840 about 30 parts by weight Suitable for electrostatic application. In special cases to eliminate spreading defects, peel or bubble formation, it is recommended to replace part of the thinner (5% to 10%) with special NXG thinner code 11764P. Activation: If needed, to increase solvent resistance without precluding the general characteristics of the product, add AD540496 activator to the paint at 0,5-1% rate. The addition of the activator may affect the final degree of opacity. The paint, once activated, should be used within 3-4 weeks stored at a temperature between 15-25 °C. A slight chromophoric reaction is possible over time of the activated paint.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Single component with possible activation

APPEARANCE OF THE FILM

Matte.

COLORS

Clear

SPECIFIC WEIGHT

0,972 Kg/l (± 0,02)

SUPPLY VISCOSITY

28” (±2) at 20 °C ASTM 4

DRY RESIDUE

44% (± 2)

DRYING

Drying - Print-free: 4-5 hours. 10 at 20 °C;   Forced Drying 40 at 160°C;

RECOMMENDED LAYERS

A cross coat

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.