Protective paint for flexible polyurethane (TPU) and PVC substrates. Characterized by high gloss, elasticity and good aging resistance.
Plastic materials: Tumbling or cleaning, if using specific primers.
Comp. A : 20070LX 100 parts by weight Comp. B : CZ.711 60 parts by weight Diluent : 276 10 - 30 parts by weight In special cases, to eliminate distension defects, peel or bubbles, 5-10% of 10304R retardant should be added. It is advisable to conduct preliminary tests to determine the right amount of retardant to use.
Two-component;
Glossy
Clear
0,98 Kg/l (± 0,05)
25” (±2) at 20 °C ASTM 4
52% (±2)
Dry dust-free - Print-free: 4-5 hours. 15 at 20 °C; Forced Drying 90’ - 120’ at 45-55 °C. 60’ – 90’ at 70-80 °C.
A cross coat
No later than 24 hours after baking in the oven
90’ the pot-life decreases at higher temperature Ultimate chemical resistances reached after 5 days (at 20 °C) after leaving the baking oven.
Strictly follow the instructions on the labeling and in the safety data sheet.
The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.