22L00501 - ACRYLIC 1K METAL TOPCOAT LT HC V2

FIELD OF APPLICATION:

Paint for the protection and decoration of metal eyeglass frames. Suitable as protective agent for brass products and general galvanic substrates (handles, fashion accessories, etc.). Direct adhesion on metal, non-yellowing, high resistance characteristics to CASS test and ISO 12870 artificial sweat.

PREPARATION OF THE SUBSTRATE:

The substrate should be free of any kind of surface contaminants, (lubricant, traces of oxidation, residues of waxes or polishing pastes, residues of substances from galvanic baths, etc.) so it should be treated with appropriate cleaning methods.

PREPARATION OF THE PRODUCT:

Comp. A : 22L00501 100 parts by weight Diluent: 11764P about 15 parts by weight Suitable for electrostatic application. Activation To increase solvent resistance without precluding the general characteristics of the product, add AD540496 activator to the paint at 1% rate. The paint once activated should be used within 3-4 weeks stored at a temperature between 15 and 25 °C A slight chromophoric reaction of the activated paint is possible over time.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Single component with possible activation

APPEARANCE OF THE FILM

Glossy

COLORS

Clear

SPECIFIC WEIGHT

0,952 kg/lt (± 0,02)

SUPPLY VISCOSITY

15.5” (±1) at 20 °C ASTM 4

DRY RESIDUE

38% (±2)

DRYING

Drying - Print-free: 4-5 hours. 10’ at 20 °C   Forced Drying 40’ at 160 °C

RECOMMENDED LAYERS

A cross coat

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.