29189SA - VERNICE OPACA

FIELD OF APPLICATION:

A protective varnish for cellulose acetate substrates, the varnish also demonstrates good adhesion on cellulose acetopropionate and Grilamid. Characterized by high softness, elasticity and good resistance to light and artificial sweat.

PREPARATION OF THE SUBSTRATE:

Plastic materials: Tumbling

PREPARATION OF THE PRODUCT:

Comp. A : 20189SA 100 parts by weight Comp. B : 10091P 30 parts by weight Diluent : 276 60-80 parts by weight NOTE: It is possible in special cases to eliminate spreading defects, peel, bubble formation, to replace part of the thinner with retardant 10304R. It is advisable to conduct preliminary tests to determine the right amount of retardant to use

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Matte

COLORS

Clear

SPECIFIC WEIGHT

1,02 kg/lt (± 0,02)

SUPPLY VISCOSITY

33” (±2) at 20 °C ASTM 4

DRY RESIDUE (A)

43% (± 2)

DRYING

Drying - Print-free: 4-5 hours. 5-10’ at 20 °C. Forced Drying 60’ at 45-55 °C.

RECOMMENDED LAYERS

A cross coat

POT-LIFE at 20 °C

> 4 hours. The pot-life decreases at higher temperature

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.