Protective varnish for Grilamid, cellulose acetopropionate, ABS and Polycarbonate substrates. Characterized by high gloss, high filling, adhesion, elasticity and good resistance to light and artificial sweat.
Plastic materials: Tumbling if necessary.
Comp. A : 203826 100 parts by weight Comp. B : 20088 50 parts by weight Diluent : 276 – 252 30 - 40 parts by weight In special cases, to eliminate distension defects, peel or bubbles, 5-10% of 10304R retardant should be added. It is advisable to conduct preliminary tests to determine the right amount of retardant to use.
Two-component;
Glossy
Clear
1,00 kg/lt (± 0,02)
24” (±2) at 20 °C ASTM 4
45% (±2)
Drying - Print-free: 4-5 hours. 50 - 10’ at 20 °C Forced Drying 40 - 60’ at 55 - 60°C
A cross coat
> 4 Hours, the pot-life decreases at higher temperature The final chemical resistances, are reached after 5 days (at 20 °C) after leaving the baking oven.
Strictly follow the instructions on the labeling and in the safety data sheet.
The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.
VERNICI CALDART SRL © 2022 | P.IVA IT00759630965 | Privacy Policy | Cookies Policy | Ethical Code | Whistleblowing | Financing | SOFTWEB