20070LX - VERNICE PER POLIURETANO

FIELD OF APPLICATION:

Protective paint for flexible polyurethane (TPU) and PVC substrates. Characterized by high gloss, elasticity and good aging resistance.

PREPARATION OF THE SUBSTRATE:

Plastic materials: Tumbling or cleaning, if using specific primers.

PREPARATION OF THE PRODUCT:

Comp. A : 20070LX 100 parts by weight Comp. B : CZ.711 60 parts by weight Diluent : 276 10 - 30 parts by weight In special cases, to eliminate distension defects, peel or bubbles, 5-10% of 10304R retardant should be added. It is advisable to conduct preliminary tests to determine the right amount of retardant to use.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Glossy

COLORS

Clear

SPECIFIC WEIGHT

0,98 Kg/l (± 0,05)

SUPPLY VISCOSITY

25” (±2) at 20 °C ASTM 4

DRY RESIDUE (A)

52% (±2)

DRYING

Dry dust-free - Print-free: 4-5 hours. 15 at 20 °C;   Forced Drying 90’ - 120’ at 45-55 °C. 60’ – 90’ at 70-80 °C.

RECOMMENDED LAYERS

A cross coat

RECOATING:

No later than 24 hours after baking in the oven

POT- LIFE at 20 °C

90’ the pot-life decreases at higher temperature Ultimate chemical resistances reached after 5 days (at 20 °C) after leaving the baking oven.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room should be dry, not exposed to the sun and with a temperature between +10 °C and +30 °C. Rev.: 06/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.