K.713 - ACRILGRIP SEMIOPACO

FIELD OF APPLICATION:

High quality finish, particularly suitable in machine tools, operating, agricultural, furniture, furniture components and plastics. It can be used directly on the substrate (iron, aluminum, galvanized sheet), as it has excellent general adhesion.

High-quality, semi-matt acrylic finish, particularly suitable for machine tools, agricultural machinery, furniture, furniture components and plastics. It can be used directly on the substrate (iron, aluminium, galvanised sheet metal) as it has excellent general adhesion.

RECOMMENDED PRIMERS:

See preparation substrate

PREPARATION OF THE SUBSTRATE:

Iron or steel sheet metal: SA2 sandblasting or sanding followed by degreasing with solvents. Aluminum and light alloys: Sanding followed by degreasing with solvents. Galvanized sheet: Scouring with Scotch-Brite followed by degreasing with solvents. PP: Flaming ABS, ABS-PC, PUR and thermosetting resins: Degreasing with suitable solvents.

Iron or steel sheet metal: SA2 sandblasting or sanding followed by degreasing with solvents. Aluminum and light alloys: Sanding followed by degreasing with solvents. Galvanized sheet: Scouring with Scotch-Brite followed by degreasing with solvents. PP: Flaming ABS, ABS-PC, PUR and thermosetting resins: Degreasing with suitable solvents.

PREPARATION OF THE PRODUCT:

Comp. A: K.713 + Coloring pastes (Ratio 80/20) 100 parts by weight 100 parts by volume Comp. B: CZ.265 or CZ.777 15 parts by weight 20 parts by volume Or: CZ.265 or CZ.777 (1) 20 parts by weight 25 parts by volume (1) Catalysis at 25% by weight is recommended if special hardness, chemical resistance and/or solvent resistance is required. You will also get a slight increase in final gloss (2-4 Gloss). Mix thoroughly until the color and consistency are uniform. Dilute with our thinner D.737 or D.219 (approx. 20% by weight on Comp. A) up to a viscosity of 18"-22" Ford 4 at 20 °C.

PRODUCT SPECIFICATIONS:

PREPARATION OF THE PRODUCT:

Comp. A: K.713 + Coloring pastes (Ratio 80/20) 100 parts by weight 100 parts by volume Comp. B: CZ.265 or CZ.777 15 parts by weight 20 parts by volume Or: CZ.265 or CZ.777 (1) 20 parts by weight 25 parts by volume (1) Catalysis at 25% by weight is recommended if special hardness, chemical resistance and/or solvent resistance is required. You will also get a slight increase in final gloss (2-4 Gloss). Mix thoroughly until the color and consistency are uniform. Dilute with our thinner D.737 or D.219 (approx. 20% by weight on Comp. A) up to a viscosity of 18"-22" Ford 4 at 20 °C.

TYPE OF PRODUCT

Two-component;

PRODUCT SPECIFICATIONS:

APPEARANCE OF THE FILM

Semi-matte

TYPE OF PRODUCT

2K Acrylic Finishes

COLORS

By choice

APPEARANCE OF THE FILM

Semi-matte

SPECIFIC WEIGHT Comp. (A)

1,46 kg/lt (± 0,05)

COLORS

By choice

SUPPLY VISCOSITY

10" (± 2") Ford 8 at 25 °C

DENSITY Comp. (A)

1,46 kg/lt (± 0,05)

DRY RESIDUE

68.5% (± 2%)

SUPPLY VISCOSITY

10" (± 2") Ford 8 at 25 °C SOLID % - VOLUME (A+B) 50% (± 2%) SOLID % - WEIGHT (A+B) 67% (± 2%)

DRYING

Dry dust-free - Print-free: 4-5 hours. 15’ at 20 °C - 25 °C - Forced Drying - Print-free: 4-5 hours. 50’ - 60’ at 70 °C

DRYING AT 20°C

Dry dust-free - Print-free: 4-5 hours. 15’ - Forced Drying - Print-free: 4-5 hours. 50’ - 60’ at 70 °C

RECOMMENDED LAYERS

A cross coat

1 (cross coat)

OPACITY

25 Gloss (± 5) depending on the color and thickness applied

25 Gloss (± 5) depending on the color and thickness applied

RECOMMENDED THICKNESS

40 - 50 µm

RECOMMENDED - DFT

40 - 50 µm

POT-LIFE AT 20 °C

4 hours. The pot-life decreases at higher temperatures

4 hours. The pot-life decreases at higher temperatures

RECOATING:

Wet-on-wet within one hour or, after 8 hours minimum and not more than 36 hours. After complete curing of the film, it is necessary to sand lightly before painting.

THEORETICAL YIELD (2)

9,4 m2/lt or 6,6 m2/kg at 50 µm dry (2) In 80/ 20 ratio with P.900.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

APPLICATION INSTRUCTIONS:

View pictograms Page 1.

RECOATING:

Wet-on-wet within one hour or, after 8 hours minimum and not more than 36 hours. After complete curing of the film, it is necessary to sand lightly before painting.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 08/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 09/24 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.