K.712 - ACRILGRIP SEMILUCIDO

FIELD OF APPLICATION:

High quality finish, particularly suitable in machine tools, operating, agricultural, furniture, furniture components and plastics. It can be used directly on the substrate (iron, aluminum, galvanized sheet), as it has excellent general adhesion.

High-quality, semi-gloss acrylic finish, particularly suitable for machine tools, agricultural machinery, furniture, furniture components and plastics. It can be used directly on the substrate (iron, aluminium, galvanised sheet metal) as it has excellent general adhesion.

RECOMMENDED PRIMERS:

See preparation substrate

PREPARATION OF THE SUBSTRATE:

Iron or steel sheet metal: SA2 sandblasting or sanding followed by degreasing with solvents. Aluminum and light alloys: Sanding followed by degreasing with solvents. Galvanized sheet: Scouring with Scotch-Brite followed by degreasing with solvents. ABS, ABS-PC, PUR and thermosetting resins: Degreasing with suitable solvents. P.P.: Flaming

Iron or steel sheet metal: SA2 sandblasting or sanding followed by degreasing with solvents. Aluminum and light alloys: Sanding followed by degreasing with solvents. Galvanized sheet: Scouring with Scotch-Brite followed by degreasing with solvents. ABS, ABS-PC, PUR and thermosetting resins: Degreasing with suitable solvents. P.P.: Flaming

PREPARATION OF THE PRODUCT:

Comp. A: K.712 + Coloring Pastes 100 parts by weight (Ratio 80/20 with paste P.) Comp. B: CZ.265 or CZ.777 20 parts by weight Or: CZ.265 or CZ.777 (1) 25 parts by weight (1) Catalysis at 25% by weight is recommended if special hardness, chemical resistance and/or solvent resistance is required. You will also get a slight increase in final gloss (2-4 Gloss). Mix thoroughly until the color and consistency are uniform. Dilute with our thinner D.737 or D.219 (approx. 20% by weight on Comp. A) up to a viscosity of 16"-18" Ford 4 at 20 °C.

PRODUCT SPECIFICATIONS:

PREPARATION OF THE PRODUCT:

Comp. A: K.712 + Coloring Pastes 100 parts by weight (Ratio 80/20 with paste P.) Comp. B: CZ.265 or CZ.777 20 parts by weight Or: CZ.265 or CZ.777 (1) 25 parts by weight (1) Catalysis at 25% by weight is recommended if special hardness, chemical resistance and/or solvent resistance is required. You will also get a slight increase in final gloss (2-4 Gloss). Mix thoroughly until the color and consistency are uniform. Dilute with our thinner D.737 or D.219 (approx. 20% by weight on Comp. A) up to a viscosity of 16"-18" Ford 4 at 20 °C.

TYPE OF PRODUCT

Two-component;

PRODUCT SPECIFICATIONS:

APPEARANCE OF THE FILM

Semigloss

TYPE OF PRODUCT

2K Acrylic Finishes

COLORS

By choice

APPEARANCE

Semigloss

DENSITY Comp. (A)

1,27 kg/lt (± 0,05)

COLORS

By choice

SUPPLY VISCOSITY

100" (± 2") Ford 8 at 25 °C

DENSITY Comp. (A)

1,27 kg/lt (± 0,05)

SOLID CONTENT

64% (± 2%)

SUPPLY VISCOSITY

12" (± 2") DIN 8 at 25 °C SOLID % - VOLUME (A+B) 47% (± 2%) SOLID % - WEIGHT (A+B) 63% (± 2%)

DRYING

Dry dust-free - Print-free: 4-5 hours. 15’ at 20 °C - 25 °C - Dry to touch - Print-free: 4-5 hours. 3.5 - 4 hours - Forced Drying - Print-free: 4-5 hours. 50’ - 60’ at 70 °C

DRYING AT 20°C

Dry dust-free - Print-free: 4-5 hours. 15’ - Dry to touch - Print-free: 4-5 hours. 3.5 - 4 hours - Forced Drying - Print-free: 4-5 hours. 50’ - 60’ at 70 °C

RECOMMENDED LAYERS

A cross coat

1 (cross layer)

OPACITY

80 Gloss (± 5) depending on the color and thickness applied

BRILLIANCE

77 Gloss (± 5) depending on the color and thickness applied

RECOMMENDED THICKNESS

40 - 50 µm

RECOMMENDED - DFT

40 - 50 µm

POT-LIFE AT 20 °C

4 hours. The pot-life decreases at higher temperatures

4 hours. The pot-life decreases at higher temperatures

THEORETICAL YIELD (2)

9,9 m2/lt or 7,2 m2/kg at 50 µm dry (2) In 80/ 20 ratio with P.900.

9,4 m2/lt or 7,3 m2/kg at 50 µm dry (2) In 80/ 20 ratio with P.900.

RECOATING:

After 6 hours minimum. Following complete curing of the film, it is necessary to sand lightly before repainting.

APPLICATION INSTRUCTIONS:

View pictograms Page 1.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

RECOATING:

After 6 hours minimum.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 08/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 09/24 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.