K.711 - ACRILGRIP LUCIDO

FIELD OF APPLICATION:

High quality finish, particularly suitable in machine tools, operating, agricultural, furniture, furniture components and plastics. It can be used directly on the substrate (iron, aluminum, galvanized sheet), as it has excellent general adhesion.

High quality finish, particularly suitable in machine tools, operating, agricultural, furniture, furniture components and plastics. It can be used directly on the substrate (iron, aluminum, galvanized sheet), as it has excellent general adhesion.

RECOMMENDED PRIMERS:

See preparation substrate

PREPARATION OF THE SUBSTRATE:

Iron surfaces: Outdoor-exposed products: to obtain adequate anti-corrosive protections, it is recommended to apply a coat of 193 series epoxy primer and 793 series acrylic primer. Indoor products: pretreatment with suitable pickling products or alternatively sanding followed by degreasing with solvents. Hot-dip galvanized iron: Pretreat with adhesion promoter (our Z.030) or with passivants. Electro-galvanized sheets: Scour with red Scotch-Brite and degrease with solvents. Aluminum: Mechanical cleaning by sanding, followed by degreasing with solvents. Thermosetting resins: Degreasing with solvents. ABS: Degreasing with suitable solvents.

PREPARATION OF THE PRODUCT:

Comp. A: K.711 + Coloring Pastes 100 parts Comp. B: CZ.265 or CZ.777 33 parts Diluent: D.737 10 - 25 parts Mix thoroughly until the color and consistency are uniform. Dilute with our thinner D.737 (approx. 20% by weight on component A) to a viscosity of 16”-20" Ford 4 at 20 °C.

PREPARATION OF THE SUBSTRATE:

Iron surfaces: Outdoor-exposed products: to obtain adequate anti-corrosive protections, it is recommended to apply a coat of 193 series epoxy primer and 793 series acrylic primer. Indoor products: pretreatment with suitable pickling products or alternatively sanding followed by degreasing with solvents. Hot-dip galvanized iron: Pretreat with adhesion promoter (our Z.030) or with passivating. Electro-galvanized sheets: Scour with red Scotch-Brite and degrease with solvents. Aluminum: Mechanical cleaning by sanding, followed by degreasing with solvents. Thermosetting resins: Degreasing with solvents. ABS: Degreasing with suitable solvents.

PRODUCT SPECIFICATIONS:

PREPARATION OF THE PRODUCT:

Comp. A: K.711 + Coloring Pastes 100 parts Comp. B: CZ.265 or CZ.777 33 parts Diluent: D.737 10 - 25 parts Mix thoroughly until the color and consistency are uniform. Dilute with our thinner D.737 (approx. 20% by weight on component A) to a viscosity of 16”-18" Ford 4 at 20 °C.

TYPE OF PRODUCT

Two-component;

PRODUCT SPECIFICATIONS:

APPEARANCE OF THE FILM

Glossy

TYPE OF PRODUCT

2K Acrylic Finishes

COLORS

By choice

APPEARANCE

Glossy

DENSITY Comp. (A)

1,01 Kg/l (± 0,05)

COLORS

By choice

SUPPLY VISCOSITY

17" (± 3") Ford 8 at 20 °C

DENSITY Comp. (A)

1,01 Kg/l (± 0,05)

SOLID CONTENT

58% (± 2%)

SUPPLY VISCOSITY

17" (± 3") Ford 8 at 20 °C SOLID % - VOLUME (A+B) 48% (± 2%) SOLID % - WEIGHT (A+B) 58% (± 2%)

DRYING

Dry dust-free - Print-free: 4-5 hours. 15’ at 20 °C – 25 °C   - Forced Drying 40’ – 50’ at 70 °C

DRYING AT 20°C

Dry dust-free - Print-free: 4-5 hours. 15’   - Forced Drying 40’ – 50’ at 70 °C

RECOMMENDED LAYERS

A cross coat

1 (cross layer)

RECOMMENDED THICKNESS

40-50 µm

40-50 µm

POT-LIFE AT 20 °C

3 hours. The pot-life decreases at higher temperatures

3 hours. The pot-life decreases at higher temperatures

THEORETICAL YIELD (1)

10,6 m2/Lt or 8,7 m2/Kg at 50 µm dry (1) In 70-30 ratio with P.900. NOTE: To obtain the best chemical resistances and high hardnesses, it is possible to proceed with oven drying at 100 °C - 110 °C for 30 minutes. To improve adhesion on "critical" metal substrates such as galvanized sheet metal, we recommend the addition of Z.287 to the extent of 3% - 4 % on Component A. In the case of sheet metal or structures with new galvanizing and/or shiny appearance, it is recommended to pre-treat with 2K epoxy primer.

9,5 m2/Lt or 8,5 m2/Kg at 50 µm dry (1) In 70-30 ratio with P.900.

RECOATING:

After 12 hours minimum. When the film has completely hardened, the surface to be painted must be lightly sanded.

APPLICATION INSTRUCTIONS:

View pictograms Page 1. NOTE: To obtain the best chemical resistances and high hardnesses, it is possible to proceed with oven drying at 100 °C - 110 °C for 30 minutes. To improve adhesion on "critical" metal substrates such as galvanized sheet metal, we recommend the addition of Z.287 to the extent of 3% - 4 % on Component A. In the case of sheet metal or structures with new galvanizing and/or shiny appearance, it is recommended to pre-treat with 2K epoxy primer.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

RECOATING:

After 12 hours minimum.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 03/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 09/24 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.