Machine tools, metal furniture, carpentry, etc. If higher chemical resistance (chemical agents, aggressive chemicals) is required, sandblasting of the substrate and catalysis with CZ.110 is recommended.
Iron surfaces: SA2 sandblasting, or thorough mechanical cleaning followed by degreasing with solvents. Galvanized steel: Scouring with Scotch-Brite, or sanding followed by degreasing with solvents. Aluminum: Mechanical cleaning by sanding, followed by degreasing with solvents. Thermosetting resins: Degreasing with solvents.
Comp. A: K.162 + Coloring pastes 100 parts by weight Comp. B: CZ.105 or CZ.110 (1) 10 - 20 parts by weight (1) Excellent chemical resistance is achieved thanks to this hardener. Mix until uniform consistency and color; Dilute with our D.150 (Standard) or D.160 (Rapid) epoxy thinner to the viscosity needed to achieve the desired degree of embossing or texture.
Two-component;
Semi-Glossy TEXTURE (with CZ.105: 60-70 Gloss at 60 °C depending on the color)
On request
1,55 Kg/l (± 0,05)
Thixotropic product
78% (± 2%)
Dry dust-free - Print-free: 4-5 hours. 30’ – 40’ Drying in depth 24 – 36 hours at 20 °C Forced Drying 50’ – 60’ at 60 °C - 80 °C
One cross coat (if applied over EPOX primer).
50 - 80 µm
11,5 m2/Lt 7,9 m2/Kg 50 µm dry
8 hours. The pot-life decreases at higher temperatures (*) Ratio 80/20 with P.900.
With CZ.105: minimum 8 hours maximum 48 hours. With CZ.110: minimum 3 hours maximum 36 hours. After 48 hours, light sanding of the film is recommended to ensure good adhesion of the top coat.
Strictly follow the instructions on the labeling and in the safety data sheet.
The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 03/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.
P.010
NEUTRAL PASTE
P.100
BLACK DYES PASTE
P.106
DEEP BLACK PASTE
P.110
OXIDE YELLOW PASTE
P.115E
ECO LEMON YELLOW PASTE
P.116
COVERING ECO LEMON YELLOW PASTE
P.119E
ECO MEDIUM YELLOW PASTE
P.200E
ECO ORANGE PASTE
P.323
BRIGHT RED PASTE
P.325
DARK RED PASTE
P.330
OXIDE RED PASTE
P.354
SOLID RED PASTE
P.400
VIOLET PASTE
P.500
BLUE PASTE
P.600
GREEN PASTE
P.701
FINE ALUMINIUM PASTE
P.703
MAGNUM ALUMINIUM PASTE
P.900
WHITE PASTE
P.250
BRILLANT ORANGE ECO
P.562
LIGHT BLUE PASTE
TP.150
BLACK PASTE
TP.156
DEEP BLACK PASTE
P.TX050
FINE-GRAINED TEXTURE PASTE
P.TX70
MEDIUM-GRAINED TEXTURE PASTE
P.TX80
COARSE-GRAINED TEXTURE
P.TX90
EXTRA COARSE-GRAINED TEXTURE PASTE
P.F115
FLUORESCENT YELLOW PASTE
P.F200
FLUORESCENT ORANGE PASTE
P.F300
FLUORESCENT RED PASTE
P.F400
FLUORESCENT PINK PASTE
P.F500
FLUORESCENT BLUE PASTE
P.F600
FLUORESCENT GREEN PASTE
P.700
FINE-GRAINED ALUMINIUM PASTE
P.710
SHINY FINE-GRAINED ALUMINIUM PASTE
P.715
FINE MEDIUM-GRAINED ALUMINIUM PASTE
P.716
LIGHT COLOUR MEDIUM-GRAINED ALUMINIUM PASTE
P.720
SHINY MEDIUM-GRAINED ALUMINIUM PASTE
P.730
SHINY MAGNUM-GRAINED ALUMINIUM PASTE
P.733
COARSE-GRAINED ALUMINIUM PASTE
P.739
MAGNUM MEGA-GRAINED ALUMINIUM
P.740
LUMINOR ALUMINIUM PASTE
P.755
EXTRA-FINE ALUMINIUM PASTE
P.758
ULTRA-FINE ALUMINIUM PASTE
P.769
FINE-GRAINED ALUMINIUM PASTE
P.801
PEARLY MEDIUM PASTE
P.803
PEARLY MEDIUM WHITE EXTRA
P.805
PEARLY SHOT GOLD PASTE
P.811
PEARLY FINE PASTE
P.812
PEARLY MAGNUM PASTE
P.813
PEARLY WHITE REFLECTIVE
P.814
PEARLY MEGA MAGNUM PASTE
P.815
PEARLY SHOT RED
P.819
PEARLY SHOT LILAC
P.825
PEARLY SHOT BLUE
P.830
PEARLY GOLD PASTE
P.835
PEARLY SHOT GREEN PASTE
P.836
PEARLY GOLD OLYMPIC PASTE
P.840
PEARLY SHOT VIOLET
P.850
PEARLY BRONZE PASTE
P.851
PEARLY BRIGHT RED
P.852
PEARLY COPPER RED
P.853
PEARLY MAGNUM RED
P.854
PEARLY RED PASTE
P.866
DARK COPPER PASTE
K.223T
TECNOPOL TIXO - SMALTO PUR 2K S.O.
K.232
POLIURETANICO IN.LE SEMILUCIDO
K.234
POLIURETANICO IN.LE OPACO
TP.016
CLEAR OXIDE YELLOW PASTE
TP.037
CLEAR OXIDE RED PASTE
TP.065
CLEAR OXIDE RED PASTE
TP.066
CLEAR OXIDE YELLOW PASTE
TP.110
OXIDE YELLOW (EX TP.111)
TP.115
LEMON YELLOW (EX TP.102)
TP.116
COVERING LEMON YELLOW (EX TP.122)
TP.119
MEDIUM YELLOW (EX TP.114)
TP.200
ORANGE (EX TP.220)
TP.323
BRIGHT RED (EX TP.370)
TP.325
DARK RED (EX TP.321)
TP.330
OXIDE RED (EX TP.300)
TP.354
SOLIDE RED (EX TP.329)
TP.400
VIOLET (EX TP.440)
TP.500
BLUE (EX TP.510)
TP.600
GREEN (EX TP.607)
TP.900
WHITE (EX 40610)
Administrative headquarters and Eyewear
Cosmetic Packaging Division
Via dell'industria, 21
20882 Bellusco (MB) - Italy
+ 39 039 684 08 50 / 53
Industry / Car Refinish Division
Via 1° maggio, 22 - Località Cagnano
36026 Pojana Maggiore (VI) - Italy
+ 39 044 476 44 15
VERNICI CALDART SRL © 2022 | P.IVA IT00759630965 | Privacy Policy | Cookies Policy | Ethical Code | Whistleblowing | Financing | SOFTWEB