K.EFT - CONVERTER PER EFT

PRODUCT DESCRIPTION:

Two-component paint made of dispersion of metallic aluminum in solvent and special resins. The innovative formulation of the EFT series finishes makes it possible to obtain coatings with final mechanical and chemical characteristics that do not require repainting with protective clear coats. Good surface hardness.

FIELD OF APPLICATION:

Elongation resin for EFT.

END USES:

Objects, cosmetics, furnishings, appliances, handicrafts and products in general designed for indoor use.

HOW TO USE:

All EFTs, except for EFT.990, can be color-modified if necessary to achieve a sample shade. This is done by the addition of Predisol series dyes up to a maximum of 5% by weight. If, for colorimetric requirements, the dosage of Predisol exceeds 5%, K.EFT should be added at a ratio of 1:4 to the amount of dye added to balance the pigment-resin ratio. EFT. Predisol K.EFT 100 0 - 5 Not necessary 100 5 - 10 20 100 10 - 15 40 100 15 - 20 60 NB: Additions above 20% are not recommended. The resulting product of the EFT mixture. Predisol and K.EFT should be catalyzed at 5% by weight with CZ.678 or CZ.711, depending on the nature of the substrate as specified in the TDS of the EFT series.

SUBSTRATE PRE-TREATMENT:

The pre-treatment of the substrate depends on the type of filler used. The product can be applied directly on some plastic materials such as, for example, ABS or ABS + PC. For metal substrates, the application of a suitable primer is recommended, preferably gloss black (to improve the metallic effect).

PRODUCT SPECIFICATIONS:

PRODUCT PRE-TREATMENT:

The paint should always be shaken before use. Comp. A : EFT. 100 parts by weight Comp. B : CZ.678 on plastic 5 parts by weight Or : CZ.711 on metal (1) 5 parts by weight (1) In the case of application on metal (such as for example polished and/or brushed aluminum or polished steel), it is necessary to add 3% by weight of Z.287. Repainting with a 2K final protective product is recommended. For detailed information regarding the direct application of EFT on metal, it is advisable to contact our Caldart Research & Development laboratory. After catalysis, the product is ready for use. To improve surface hardness and scratch resistance, we recommend adding 1 - 2% of Z.070.

TYPE OF PRODUCT

Two-component;

PRODUCT SPECIFICATIONS:

APPEARANCE OF THE FILM

Satin

TYPE OF PRODUCT

Two-component

COLORS

Colorless

FILM ASPECT

Satin

DENSITY

0,90 Kg/l (± 0,02)

COLOURS

Various

SUPPLY VISCOSITY

11" (± 2) ASTM 4 at 20 °C

DENSITY

0,90 Kg/l (± 0,02)

SOLID CONTENT

5% (± 1)

DELIVERY VISCOSITY

11” (± 2) ASTM 4 at 20 °C

DRYING

Dry dust-free - Print-free: 4-5 hours. 3’ – 5’   Print-free 10’ at A.T.   Curing 40’ at 50 °C – 60 °C.

SOLID CONTENT

5% (± 1)

STORAGE:

Store at temperatures between +5 to +30 °C.

CURING TIME AT 20°C.

Dust free 3’ - 5’ at A.T. Touch dry 10’ at A.T. Hardening 40’ at 50°C - 60°C

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet. Rev.: 03/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

THEORETICAL YIELD

2,5 - 2,8 m2/Lt with two layers

RECOATABILITY

Wet on wet consigliata spece se Dopo indurimento la riverniciabilir

RECOMMENDED LAYERS

2-3 layers

POT-LIFE : 2 hours at 20°C

RECOATABILITY:

In case you want to increase the abrasion resistance or more generally the chemical-physical resistance of the film, it is possible to cover it with 2K acrylic paints like our glossy 701.00020 or 701.00015 or the matt 704.00020.

SAFETY STANDARDS:

Read and carefully follow the instructions on the label and in the safety data sheet.

STORAGE CONDITIONS:

In unopened and sealed packages, kept at a temperature between +5°C +30°C. Rev.: 03/22 Data and information contained in this technical data sheet are the result of our experience and accurate laboratory tests. However, since the painting process is a set of operations that are beyond our control, they therefore in no way constitute any form of guarantee on the final performances of the cycle itself.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.