Preparation of the substrate depends on the type of material to be painted. The surface must be previously painted with a glossy-looking and perfectly leveled enamel or primer + enamel. Particularly suitable for metal substrates are the enamels obtained from K.111 and P.EP or P series pastes. Possible to use 701.00020 as undercoat preparation. For ABS or ABS-PC substrates, use 701.00015 colored with TP pastes.
Paint should always be stirred before use. Comp. A : EFT.990 100 parts by weight Comp. B (optional) : CZ.678 2 parts by weight It can be used as 1K only on undercoat from K.111 (P.EP). EFT.990 always needs to be repainted with final protective clear coat.
1K with a possibility of 2K
Satin
Silver-plated
0,90 Kg/l (± 0,02)
11” (± 2) ASTM 4 at 20 °C
5% (± 1)
Dry dust-free - Print-free: 4-5 hours. 3’-5’ at A.T Print-free - Print-free: 4-5 hours. 10’ at A.T Curing - Print-free: 4-5 hours. 30’ at 60 °C
1 - 2 m2/Lt two coats
Wet-on-wet recommended especially if After curing the repainting
2 - 3 coats
EFT.990
METAL
1K K.111 / P.EP106 Ratio 80-20 35% CZ.105 Dil. 50% D.150 1 hour a.t. + 1 hour at 60 °C or 24 hours A.T. 701.00015 90/10 TP.150 45% CZ.280 24 hours a.t. Ready-to-use 2 coats 1 hour at a.t. or 30’ at 60 °C 701.00020 33% CZ.265 Dil. 80% D.737 two coats 10/15 min apart. Final baking 1 hour at 60 °C 2K K.111 / P.106 Ratio 70-30 33% CZ.105 Dil. 50% D.150 1 hour a.t. + 1 hour at 60 °C or 24 hour a.t. EFT.990 Cat. 2% with CZ.678 2 coats 1 hour at a.t. or 30’ at 60 °C 701.00020 33% CZ.265 Dil. 80% D.737 two coats 10/15 min apart. Final baking 1 hour at 60 °C 701.00020 33% CZ.265 Dil. 30% D.737 1 hour at 60 °C
Recoatable after 1 hour at A.T., or after 30 minutes at 60 °C with 701.00020.
Strictly follow the instructions on the labeling and in the safety data sheet.
In unopened and sealed packages, kept at temperatures between +5 °C to +30 °C. Rev.: 10/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.
The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.
EFT.113
2K TITANIUM EFFECT
EFT.114
2K NICKEL EFFECT
EFT.115
2K BLACK NICKEL EFFECT
EFT.350
2K COPPER EFFECT
EFT.351
2K LIGHT COPPER EFFECT
EFT.397
2K Antique Bronze EFFECT
EFT.451
2K Antique Gold EFFECT
EFT.740
2K DUCAL GOLD SATIN EFFECT
EFT.750
2K GOLD EFFECT
EFT.850
2K BRONZE EFFECT
EFT.860
2K DARK BRONZE EFFECT
EFT.900
2K SILVER EFFECT
EFT.980
2K Pearl Satin EFFECT
22801C
PREDISOL CONCENTRATE VIOLET
22805C
PREDISOL CONCENTRATE BLACK
22808C
PREDISOL CONCENTRATE BLEU
22809
PREDISOL RED
22822
PREDISOL YELLOW
22832
PREDISOL YELLOW CHIP
22839
MAGENTA PREDISOL
22849
PREDISOL RED CHIP
STP.1150
Superpredisol Cold Yellow
STP.3122
Superpredisol Pink
STP.3179
Superpredisol Rubin Red
STP.5108
Superpredisol Cyano Blue
STP.5151
Superpredisol Electric Blue
STP.9007
SUPERPREDISOL BLACK
50103M
DARK BROWN CONCENTRATED COLOURANT
50104M
BRIGHT ORANGE CONCENTRATED COLOURANT
50105M
BLACK CONCENTRATED COLOURANT
50107M
GREEN CONCENTRATED COLOURANT
50108M
TURQUOISE CONCENTRATED COLOURANT
50111M
PINK CONCENTRATED COLOURANT
50113M
DARK RED CONCENTRATED COLOURANT
50114M
YELLOW OCHRE CONCENTRATED COLOURANT
50118M
BLUE CONCENTRATED COLOURANT
50119M
RED CONCENTRATED COLOURANT
50123M
DARK RED CONCENTRATED COLOURANT
50124MX
NEW SCARLET CONCENTRATED COLOURANT
50131M
VIOLET CONCENTRATED COLOURANT
50134M
ORANGE CONCENTRATED COLOURANT
50141M
BORDEAUX CONCENTRATED COLOURANT
50142M
BRIGHT YELLOW CONCENTRATED COLOURANT
50143M
DARK BROWN CONCENTRATED COLOURANT
50148M
DEEP BLUE CONCENTRATED COLOURANT
50165M
BLACK CONCENTRATED COLOURANT
VERNICI CALDART SRL © 2022 | P.IVA IT00759630965 | Privacy Policy | Cookies Policy | Ethical Code | Whistleblowing | Financing | SOFTWEB