719.90900 - MULTIGRIP - ACRILICO BIANCO BASE

FIELD OF APPLICATION:

High quality finish; Especially suitable for direct coating of plastic substrates (ABS, ABS+PC, PUR, PU, PF), and also metals such as steel, galvanized steel, brass, zamak. Also recommended for glass applications, especially for outdoor. Given the variety of glasses on the market anyway, a preliminary adhesion test is always recommended. 711.90900 has a controlled colorimetric yield so it can be used as a colorable white base coat up to a maximum of 5% P. paste for making pastel shades.

PREPARATION OF THE SUBSTRATE:

Thermosetting resins (PU, PF): Degreasing with solvents. ABS, ABS+PC: Degreasing with suitable solvents. PP: Flaming and/or primer 66003 or 66099, if necessary (1). Metals in general: Degreasing with solvents followed by sanding or buffing. (1) Normally it is not necessary to apply primer; however given the wide variety of PP and its mixtures on the market, it is recommended to do some preliminary testing before moving on to large scale productions.

PREPARATION OF THE PRODUCT:

Comp. A: 719.90900 100 parts by weight Comp. B: CZ.265 15 parts by weight (or 20 parts (2)) Alternatively: CZ.711 (2) 20 parts by weight (2) The use of CZ.265 and CZ.711 at 20% by weight is recommended if the finish is used as a single coat. By doing so, greater hardness, chemical resistance and solvent resistance are achieved. With these catalyses, however, there will be a slight increase in the final gloss (2 - 4 Gloss). Dilute with our thinner D.737 - D.219 (approx. 20% by weight on A) to a viscosity of 18-20" Ford 4 at 20 °C.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Semi-matte

COLORS

Controlled white

SPECIFIC WEIGHT (Comp. A)

1,44 Kg/l (± 0,05)

SUPPLY VISCOSITY

13" (± 2) DIN 8 at 25 °C

DRY RESIDUE (Comp. A)

68% (± 2)

DRYING

Dry dust-free - Print-free: 4-5 hours. 15’ at 20 - 25 °C

Print-free - Print-free: 4-5 hours 3 hours   Forced Drying 50’ - 60’ at 70 °C.

RECOMMENDED LAYERS

A cross coat

OPACITY

30 Gloss (± 2) (when applied as a single coat to finish).

RECOMMENDED THICKNESS

40 - 50 micron

POT- LIFE AT 20 °C

4 hours. The pot-life decreases at higher temperatures

THEORETICAL YIELD

9,2 m2/Lt or 6,8 m2/Kg at 50 micron dry

RECOATING:

Wet-on-wet within 1 hour, or, after 8 hours minimum and not more than 36 hours. After complete curing of the film, it is necessary to sand lightly before repainting.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 03/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.