application datasheet

application datasheet

Download sheet in pdf

901.00020 - TRASPARENTE LUCIDO 2C ACIDOINDURENTE

View Product Shelf Life

PREPARATION OF THE SUBSTRATE:

The substrate should be free of any kind of surface contaminants, (grease, traces of oxidation, residues of waxes or polishing pastes, residues of substances from galvanic baths, etc.) so it should be treated with appropriate cleaning methods.

PREPARATION OF THE PRODUCT:

Comp. A: 901.00020 100 parts Diluent: D.921 55 – 65 parts Compatible with electrostatic application systems. In special cases to eliminate distension defects, peel, bubble formation, add 3-5% retardant 10063.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Two-component;

APPEARANCE OF THE FILM

Glossy

COLORS

Clear

SPECIFIC WEIGHT

0,94 Kg/L (± 0,05)

SUPPLY VISCOSITY

70” (± 5”) at 20 °C ASTM 4

DRY RESIDUE (comp.A)

32% (± 2)

DRYING

Dry dust-free - Print-free: 4-5 hours. 10’ - 15’   Forced Drying (1) 30’ at 90 °C   Maximum resistance After 10 days

RECOMMENDED LAYERS

Two coats

RECOMMENDED THICKNESS

15 - 20 micron

RESISTIVITY

3 M? (± 1) (1) The product also dries at room temperature, however, to achieve the best possible chemical and adhesion strengths, we recommend baking in an oven at 100 °C for 30 minutes minimum. Features of the cured film (30‘ at 90 °C + 72 hours A.T.): König Hardness: (t2 glass Caldart in-house method) 135” Resistance to ethyl alcohol: (Caldart in-house method) 100 double applications No alteration Resistance to acetone: ((Caldart in-house method) 20 double applications No alteration NOTE: If necessary, the paint can be colored with our 50100M series color concentrates at the rate of 1-3% referred to 100 parts of undiluted paint. Larger additions are also possible, however, we recommend preliminary testing of the suitability of the complete cycle before moving to industrial-scale production. Not recommended for products in contact with water or exposed in high relative humidity environments.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

In unopened and sealed packages, kept at a temperature of +5 to +30 °C. Rev.: 05/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.

Other products in PRODOTTI PER LEGHE

 > 2K ACRYLIC CLEAR COATS

701.00020

ULTRALACK 2K GLOSS

Vernici per Metalizzazione Sputtering PVD
Leghe Metallo Plastica Vetro

701.00080

ULTRALACK 2K TRASP. LUC. NO STAGNO

Vernici per Metalizzazione Sputtering PVD
Leghe Metallo Plastica Vetro

704.00020

ULTRALACK 2K MATT

Leghe Metallo Plastica Vetro
 > STOVING CLEAR COATS 140 °C

801.14061

STOVING CLEAR COATS 140° GLOSS

Leghe Metallo Vetro

803.14063

STOVING CLEAR COATS 140° SEMI-MATT

Leghe Metallo Vetro

804.14062

STOVING CLEAR COATS 140° MATT

Leghe Metallo Vetro
 > STOVING CLEAR COATS 160 °C

820006

MATT EPOXY CLEAR COAT

Leghe Metallo Vetro

820011

GLOSS EPOXY CLEAR COAT

Leghe Metallo Vetro
 > NITRO-ACRYLIC CLEAR COAT

511.00050

GLOSS NITRO-ACRYLIC CLEAR COAT

Metallo
 > 2K CLEAR COATS

904.00030

2K MATT ACID-HARDENER CLEAR COAT

Leghe Metallo Vetro